Self-adhesive film series 352



Thickness* (without protective paper and adhesive)

0,023 mm (black, chrome, Matt chrome, shiny gold and shiny gold c two sides)

0,050 mm (white, chrome, silver, polished finish, double-sided glossy gold)

Dimensional stability (FINAT TM 14)
Adhered to steel in the transverse direction, there is no measurable shrinkage in the longitudinal direction is 0.1 mm max.
Adhered to aluminium, -40°C to +120°C
Resistance to sea water (DIN 50021)
Adhered to aluminium, after 100 h./23°C without changes
Adhesive force*, (FINAT-TM1 after 24 hours, stainless steel)
12 N/25 mm
Tensile strength (DIN EN ISO 527)

In the longitudinal direction: 200 MPa min.
In the transverse direction: 260 MPa min.

Elongation at break (DIN EN ISO 527)

In the longitudinal direction: min. 125 %

In the transverse direction: min. 80 %

Shelf life**
2 years
Bonding temperature
> +8° C
Lifetime when properly processed
2 years, " glossy gold 1 year
* average ** in original packaging, at 20°C and 50% relative humidity *** normal climate of Central Europe.


Transparent, white or metallized polyester film with excellent dimensional stability and good behavior during aging. Surface treated for printing.

The substrate

Silicone coated paper with double-sided PE-coated, 160 g/m2.


Polyacrylate adhesive is a solvent-based, providing permanent adhesion


For the manufacture of high-quality labels, personal identification and technical plates, decorative plates and warning labels.

Printing method

Recommended screen printing and UV offset printing.


The basis on which the gluing must be free from dust, grease and other contaminants that can adversely affect the bond strength of the material. When printing, the ink should be dried and cured completely. To determine the compatibility be applied must be thoroughly tested with provided paints.

The batch traceability according to ISO 9001 is possible on the basis of the roll number.